49% Translucency UT Amann Girrbach Anterius Zirconia Milling Disc 98*16MM
Stipes Yurucheng zirconia altam vim habet, praestantem permeabilitatem et colorem aestheticam reparationis effectum, qui rationi et systemati manuali aptus est.
-
Dental Lab Use UT Multilayer Zirconia Obstructionum optimum vexillum altum translucency49%
Alta transmissio 49%, maxime utens pro Veneer
-
Dental Lab Colorful Pre Shaded UT Multilayer Zirconia Clausus
Characteres corporei
Densitas inserta: 6.07±0.01g/cm³
Tendens virtus: DC MPa
Transmissio: 49%
Duritia: 1250HV
Sintering temperies: 1480~1550℃/ commendare 1500℃
-
1250HV 600Mpa 49% Multilayer Zirconia Disc
Characteres corporei
Densitas inserta: 6.07±0.01g/cm³
Tendens virtus: DC MPa
Transmissio: 49%
Duritia: 1250HV
Sintering temperies: 1480~1550℃/ commendare 1500℃
-
ISO/CE Approbata dentalis implantatio plena Zirconia obstruit Pro Corona 49% High Translucens Alba Zirconium Blank enim dentalis Laboratory
Features of 49% UT altum zirconium translucens blank:
1.Ultra translucens
2.Suitable pro crusta, parietum, pontis 1-3units
3.Bending vires: 600MPa
4.Translucency: 49%
-
Falsi dentes yucera dentalis zirconia vestis UT 98*14 discus totus ceramicus ad systema apertum CAD CAM
Nostra producta sunt zirconia denture ceramicae, respondentes CADCAM apparatu,3D instrumento excudendi et aliis oralis oralis productis affinis. Sicut materias professionales orales suppeditare, possumus providere materiae dentalis digitalis, dentis instrumenti, dentalis programmatis et plenae range of digital products et officia.
Nostrae zirconiae caudices dentales / blank compatiuntur cum diversis notis systematis CAD/CAM et systematis manualibus, ut systema Zircon, systema sirona Inlab, systema Kavo, ratio Amann Girrbach, et systema Porland, etc.
-
1500 Degree Dental Zirconia Disc Lab UT Zirconia Ceramic Blocks
YUCERA codicellos fiunt ex zirconiumdioxyde biocompatibili.Yttrium oxydatum stabiliens materiam contra rimas tuetur et vires distrahens et compressivas auget.Praecipua magnitudinis destinatio frumenti intra materiam et oxydatum aluminium additum etiam in extra vires in millingendo et postea in usu clinico evenit.Praeclarae notae mechanicae, excellentes diuturnitas chemica et invicta biocompatibilitas, cum praedestinatione translucens color YUCERA sicut idealis provisor materialis systematis millingendi dentalis.
-
Qualitas princeps UT- zirconia scandalum ceramic indenturae cum technica pretio
UT Dental Zirconia Blank Introduction
Stipes Yurucheng zirconia altam vim habet, praestantem permeabilitatem et colorem aestheticam reparationis effectum, qui rationi et systemati manuali aptus est.