98x10mm White 1200MPA Dental Zirconia Blank For Lab

Short Description:

HT Zirconia Block

*High translucent

*Brilliant bending strength and economic block

*Suitable for coping and framework


Product Detail

Product Tags

YUCERA Dental Materials And Equipment Manufacturer Economical Dental Zirconia Blanks For Dental Laboratory


To achieve expected quality, the sintering curves for dental zirconia blanks must be followed.

Note: please employ high-temperature furnace specially designed for denture manufacturing. It is good for ceramics sintering to prolong heating up time and cooling time properly.

1. Sintering preparation: Make sure there is enough sintering space to avoid deformation. After dyeing, the restoration must be dried. Do not heat up too quickly for it might result in cracks. Make sure the dust-proof cover is put on the crucible to keep impurity away from restorations

2. After sintering: Following the instruction to lower temperature and take out restorations. Do not reduce furnace temperature too quickly to avoid cracks.

3.The highest temperature: the highest temperature will affect the translucency and dyeing results. Make sure the accurate temperature of every step. Sinter and preserve heat according to the instruction.

Zirconia Block Introduction

Yucera zirconia block has high strength, excellent permeability and color aesthetic repair effect that suitable for CAD/CAM system and manual system.


Dental Zirconia Blanks Features

Safety:No irritation,No corrosion,Good bio-compatibility

Beauty:Natural teeth color can be reproduced

Comfortability:Low thermal conductivity,hot and cold changes do not stimulte the pulp

Durability:Over 1600MPa perturbed strength, durable and useful


HT Zirconia Block

*High translucent

*Brilliant bending strength and economic block

*Suitable for coping and framework


Indications of dental zirconia blanks

Coping, Inlay, Onlay, Bridge, Crown


Physical Characteristics of dental zirconia blanks

Physical Characteristics
Sintered density 6.07±0.01g/cm³
Bending Strength 1200 MPa
Transmittance 41%
Hardness 1200HV
Sintering temperature 1480~1550℃/recommend 1530℃